partial replacement of aggregate with waste glass

partial replacement of aggregate with waste glass

  • AN EXPERIMENTAL STUDY ON WASTE GLASS AS PARTIAL ...

    detrimental to the environment. Using waste glass in concrete has gained far more importance in parallel to environmental consciousness. In this project an attempt has been made to use the waste glass as partial replacement for both fine aggregate and coarse aggregate separately. For this M 20 grade of

  • Recycling of waste glass as a partial replacement for fine ...

    The properties of concretes containing waste glass as fine aggregate were investigated in this study. The strength properties and ASR expansion were analyzed in terms of waste glass content. An overall quantity of 80 kg of crushed waste glass was used as a partial replacement for sand at 10%, 15%, and 20% with 900 kg of concrete mixes. The ...

    Cited by: 204
  • Study of Concrete Involving Use of Waste Glass as Partial ...

    Study of Concrete Involving Use of Waste Glass as Partial Replacement of Fine Aggregates iosrjen.org 10 P a g e 4.2. Hardened concrete The compressive strength tests and splitting tensile strength tests are presented in TABLE 3.

    Published in: IOSR Journal of Engineering 2013Authors: M Iqbal Malik Muzafar Bashir Sajad Ahmad Tabish Tariq Umar Chowdhary
  • Partial Replacement of Cement and Fine Aggregate by using ...

    waste glass. When concrete mix with cement substituted bentonite and fine aggregates with recycled waste glass shows slump reduction than the control mix as shown in table I. TABLE I WORKABILITY RESULTS OF ALL MIXES Mix Partial Replacement of Cement by Bentonite % Partial Replacement of Sand by Glass Aggregate % Slump in mm MX 01

  • Recycling of Waste Glass as A Partial Replacement for Fine ...

    This results determined the permissibility of using waste glass as partial replacement of coarse aggregates up to 20% by weight glass can be used as an alternate construction material to coarse ...

  • Study of Concrete Involving Use of Waste Glass as Partial ...

    iosrjen.org 8Pa g e Study of Concrete Involving Use of Waste Glass as Partial Replacement of Fine Aggregates This paper summarized the behavior of concrete involving replacement of fine aggregates by waste glass as 10%, 20%, 30% and 40 % by weight which may help to reduce the disposal problems of waste glass and enhance properties of concrete.

  • PARTIAL REPLACEMENT OF COARSE AGGREGATE ... -

    PDF The possibility of using broken glass as a substitute for coarse aggregate in concrete serves as one of the possible solutions to the escalating solid waste problem. The disposal of solid ...

  • Recycled glass as a partial replacement for fine aggregate ...

    fits may be derived from incorporating waste glass as a replacement for fine aggregate, with particle size limited to ensure detrimental ASR effects are mitigated. Recent studies which have focused on the suitabil-ity of using waste glass as a partial replacement for fine aggregate

    Authors: Matthew Adaway Ying WangAffiliation: Deakin UniversityAbout: Waste management Compressive strength
  • EXPERIMENTAL INVESTIGATION OF WASTE GLASS POWDER

    Like PFA and GGBS a waste glass powder (GLP) is also used as a binder with partial replacement of cement which take some part of reaction at the time of hydration, also it is act as a filler material. In this study, waste glass powders have been used as replacements to the concrete ingredient

  • Waste glass powder as partial replacement of cement for ...

    Glass is principally composed of silica. Use of milled (ground) waste glass in concrete as partial replacement of cement could be an important step toward development of sustainable (environmentally friendly, energy-efficient and economical) infrastructure systems.

  • Partial Replacement of Fine Aggregates by using Waste

    the permissibility of using waste glass powder as partial replacement of fine aggregates up to 20% by weight for particle size of range 0-1.18mm. We estimate increase in slump value, compaction factor and compressive strength Keywords – sustainability, waste glass powder, replacement of sand I. INTRODUCTION

  • Study of Concrete Involving Use of Waste Glass as Partial ...

    iosrjen.org 8Pa g e Study of Concrete Involving Use of Waste Glass as Partial Replacement of Fine Aggregates This paper summarized the behavior of concrete involving replacement of fine aggregates by waste glass as 10%, 20%, 30% and 40 % by weight which may help to reduce the disposal problems of waste glass and enhance properties of concrete.

  • Partial Replacement of Fine Aggregate Coarse Aggregate ...

    Partial Replacement of Fine Aggregate Coarse Aggregate by Waste Glass Powder Coconut Shell Kumar Animesh1, Jeet Tiwari2, Kapil Soni3 1M.tech Scholar, Department of Civil Engineering , Institute of Technology Aisect University, Raisen (M.P.) India

  • Partial Replacement of Fine Aggregates with Waste Glass

    Partial Replacement of Fine Aggregates with Waste Glass, International Journal of Advance Research, Ideas and Innovations in Technology, IJARIIT. APA Ishan Srivastava, Dushyant Gupta, Sukhvinder Singh Sehmi, Kumar Shivam, Jhalki Bharadwaj (2017). Partial Replacement of Fine Aggregates with Waste Glass.

  • Partial Replacement of Fine Aggregates with Waste Glass

    [8] Experimental Studies on Replacement of Fine Aggregate with Glass and Fly Ash M.S.Kuttimarks1, R.Shruthi2, International Journal of Emerging Engineering Research and Technology Volume 2, Issue 2, May 2014, PP 205-208. [9] Study of Concrete Involving Use of Waste Glass as Partial Replacement of Fine Aggregates M. Iqbal Malik,

  • Partial Replacement of Lime Sludge and Glass Powder by ...

    The results concluded the permissibility of using waste glass powder as partial replacement of fine aggregates up to 30% by weight for particle size of range 0-1.18mm. 20% replacement of fine aggregates by waste glass showed 15% increase in compressive strength at 7 days and 25% increase in compressive strength at 28 .

  • ISSN: 2454-1362, onlinejournal Partial ...

    The experimental results by replacement of coarse aggregate up to 15% by waste tire have shown remarkable improvement in the physical properties of coarse aggregate. The experimental results also stated that fine aggregate can be replaced up to 10% by waste glass. Keywords- Aggregate

  • Use of glass wastes as fine aggregate in Concrete - jairjp

    1. While using waste glass as fine aggregate replacement, 28 d strength is found to marginally increase up to 20% replacement level.IV 2. Marginal decrease in strength is observed at 30 to 40% replacement level of waste glass with fine aggregate. 3. Waste glass can effectively be used as fine aggregate replacement. 4.

  • Strength and durability of recycled aggregate concrete ...

    cement paste and the interfacial transition zones in recycled aggregate concrete. Use of milled waste glass, as partial replacement of cement, is estimated to produce significant gains in strength and durability of recycled aggregate concrete. Milled waste glass

    Published in: Construction and Building Materials 2012Authors: Roz Ud Din Nassar Parviz SoroushianAffiliation: Michigan State UniversityAbout: Pozzolan Durability
  • Experimental Study of Partial Replacement of Fine ...

    protecting the environment form pollution This paper deals with partial replacement of fine aggregate with the industrial waste from China Clay industries. The compressive strength, split tensile strength and flexural strength of conventional concrete and fine aggregate replaced concrete are compared and the results are tabulated.

  • PERFORMANCE OF CONCRETE WITH PARTIAL

    The study investigated the level of replacement of fine aggregate with waste glass that will result in optimal compressive strength. A total of 36 cubes were cast. 6 cubes without waste glass (control) and 30 cubes containing waste glass as partial replacement for fine aggregates at 15%, 25%, 35%, 45%, and 50%. Water/cement ratio of 0.6 was used.

  • Partial Replacement of Fine Aggregate and Coarse

    Partial Replacement of Fine Aggregate and Coarse Aggregate by Waste Glass Powder and Coconut Shell 1D.Manimozhi, 2S.Govindhan, 3G.Sountharya 1PG Scholar, M.E-StructuralEngineering, Department of CivilEngineering, SembodaiR.V Engineering College,Sembodai,Nagappattinam, Tamilnadu-614820 2HOD,Head of the Department

  • Use of Recycle Aggregate as a Partial Replacement of ...

    Use of Recycle Aggregate as a Partial Replacement of Coarse Aggregate and Glass Powder as a Fine Aggregate Sanjay Sharma1 Sapna Verma2 1Senior Pavement Engineer 2Assistant Professor 1Egis India Consulting Engineers Pvt. Ltd 2Laxmi Narian College of Technology Abstract—The amount of waste glass has gradually

    Published in: International Journal for Scientific Research and Development 2015Authors: Sanjay Sharma Sapna Verma
  • Use of Recycle Aggregate as a Partial Replacement of ...

    Use of Recycle Aggregate as a Partial Replacement of Coarse Aggregate and Glass Powder as a Fine Aggregate Sanjay Sharma1 Sapna Verma2 1Senior Pavement Engineer 2Assistant Professor 1Egis India Consulting Engineers Pvt. Ltd 2Laxmi Narian College of Technology Abstract—The amount of waste glass has gradually

    Published in: International Journal for Scientific Research and Development 2015Authors: Sanjay Sharma Sapna Verma
  • Strength and durability of recycled aggregate concrete ...

    cement paste and the interfacial transition zones in recycled aggregate concrete. Use of milled waste glass, as partial replacement of cement, is estimated to produce significant gains in strength and durability of recycled aggregate concrete. Milled waste glass

    Published in: Construction and Building Materials 2012Authors: Roz Ud Din Nassar Parviz SoroushianAffiliation: Michigan State UniversityAbout: Pozzolan Durability
  • Experimental Study of Partial Replacement of Fine ...

    protecting the environment form pollution This paper deals with partial replacement of fine aggregate with the industrial waste from China Clay industries. The compressive strength, split tensile strength and flexural strength of conventional concrete and fine aggregate replaced concrete are compared and the results are tabulated.

  • PERFORMANCE OF CONCRETE WITH PARTIAL

    The study investigated the level of replacement of fine aggregate with waste glass that will result in optimal compressive strength. A total of 36 cubes were cast. 6 cubes without waste glass (control) and 30 cubes containing waste glass as partial replacement for fine aggregates at 15%, 25%, 35%, 45%, and 50%. Water/cement ratio of 0.6 was used.

  • Studies on Glass Powder as Partial Replacement of Cement ...

    partial replacement of cement by waste glass powder of particle size 75µm.The the waste glass powder was replaced by 10%, 20%, 30% and 40% of the binder and the mix design was prepared. The physical and chemical characteristic was studied and the chemical components of the glass powder used in the concrete were also determined by XRF (IIker ...

  • Partial Replacement Cement in Concrete Using Waste Glass

    Partial Replacement Cement in Concrete Using Waste Glass. Partial Replacement Cement in Concrete Using Waste Glass. N.Kumarappan. Student, Department of Civil Engineering (B.E, civil engineering), Chendhuran engineering college Pudukkottai, Tamilnadu State India.

  • (PDF) Partial Replacement Of Fine Aggregate By Using Glass ...

    One of its significant contributions is to the construction field where the waste glass was reused for concrete production. The properties of concretes glass dust waste as fine aggregate were investigated in this study. Glass dust waste was used as a partial replacement for

  • Comprehensive literature review on use of waste product in ...

    percentage replacement in concrete. Emphasizes on the possibility of using finely ground waste glass as partial natural sand replacement in concrete. Using waste glass, as coarse aggregate in concrete, did not have a marked effect on the workability of concrete, but the compressive strength decrease in proportion to an increase in waste glass.

  • Effect of Substitution of Crushed Waste Glass as Partial ...

    Reusing of waste glass in concrete production is among the attractive option of achieving waste reduction and preserving the natural resources from further depletion thereby protecting the environment and achieving sustainability. This present study examines the possible reuse of waste glass crushed into fine and coarse aggregate sizes as partial substitute for natural fine and coarse ...

  • partial replacement of fine aggregate by glass powder in ...

    Apr 05, 2015  PARTIAL REPLACEMENT OF FINE AGGREGATE BY GLASS POWDER IN CONCRETE 2. OBJECTIVE: To evaluate the utility of glass powder as a partial replacement of fine aggregate in concrete. To study and compare the performance conventional concrete and glass powder concrete. To understand the effectiveness of glass powder in strength enhancement.

  • GLASS DA 30.07.2016 - SlideShare

    Nov 07, 2016  GLASS DA 30.07.2016 1. DESIGNING CONCRETE MIX OF M25 GRADE BY PARTIAL REPLACEMENT OF FINE AGGREGATE WITH CRUSHED GLASS WASTE Presented By Sanjay T. Chaurasiya Guided by : Prof. Swati Kotulkar Pai Sem-14, Dissertation M.

  • PARTIAL REPLACEMENT OF CEMENT IN CONCRETE USING

    PARTIAL REPLACEMENT OF CEMENT IN CONCRETE USING WASTE GLASS POWDER AND M-SAND AS FINE AGGREGATE Shruthi.S1, Chandrakala S2, G Narayana3 1Post graduate student, Department of civil engineering, SJCIT Chickaballapur, Karnataka, India 2Assistant professor, Department of civil engineering, SJCIT College Chickaballapur, Karnataka, India

  • PARTIAL REPLACEMENT OF FINE AGGREGATE BY GLASS ...

    could be used an alternate material for natural sand as partial replacement. In brief, successful utilization of glass as fine aggregate will turn this waste material into a valuable resource. In this research we are going to evaluate the utility of glass powder as a partial replacement of fine aggregate

  • Strength and behavior of self Compacting Concrete with ...

    Using waste crushed window glass as a partial aggregate replacement with the same size of aggregate (4.75-12.5 mm) was used. Figure (1) shows the sample of the crushed glass waste which was crushed by using Loss Anglos machine. After crushing the glass, it was washed by water for removing the dust and other materials

  • Use of glass wastes as fine aggregate in Concrete - jairjp

    1. While using waste glass as fine aggregate replacement, 28 d strength is found to marginally increase up to 20% replacement level.IV 2. Marginal decrease in strength is observed at 30 to 40% replacement level of waste glass with fine aggregate. 3. Waste glass can effectively be used as fine aggregate replacement. 4.

  • partial replacement of fine aggregate by glass powder in ...

    Apr 05, 2015  PARTIAL REPLACEMENT OF FINE AGGREGATE BY GLASS POWDER IN CONCRETE 2. OBJECTIVE: To evaluate the utility of glass powder as a partial replacement of fine aggregate in concrete. To study and compare the performance conventional concrete and glass powder concrete. To understand the effectiveness of glass powder in strength enhancement.

  • Partial Replacement of E- Waste with Coarse Aggregate in ...

    Partial Replacement Of E- Waste With Coarse Aggregate In Concrete: An Investigation 1st National Conference on Technology 22 Page Maulana Mukhtar Ahmed Nadvi Technical Campus (MMANTC), Mansoora, Malegaon Maharashtra, India (GLP) for incorporation into concrete as a pozzalanic material.

  • Experimental Investigation Of Waste Glass Powder As The ...

    waste glass that is crushed and screened is a strong, safe and economical alternative to sand used in concrete. The study indicated that waste glass can effectively be used as fine aggregate replacement without substantial change in strength. Indexed Terms -- Glass, recycling, concrete, fine aggregate, waste glass. I. INTRODUCTION 1.

  • Experimental Study on Partial Replacement of Coarse ...

    Experimental Study on Partial Replacement of Coarse Aggregate with Ceramic Tile Wastes and Cement with Glass Powder B.Kavitha*, M. Lenin Sundar Department of Civil Engineering, Sri Krishna College of Technology, Coimbatore, India Abstract : This present world is very much depends on the concrete for the construction of

  • Comprehensive literature review on use of waste product in ...

    percentage replacement in concrete. Emphasizes on the possibility of using finely ground waste glass as partial natural sand replacement in concrete. Using waste glass, as coarse aggregate in concrete, did not have a marked effect on the workability of concrete, but the compressive strength decrease in proportion to an increase in waste glass.

  • Strength and behavior of self Compacting Concrete with ...

    Using waste crushed window glass as a partial aggregate replacement with the same size of aggregate (4.75-12.5 mm) was used. Figure (1) shows the sample of the crushed glass waste which was crushed by using Loss Anglos machine. After crushing the glass, it was washed by water for removing the dust and other materials

  • Partial replacement of fine aggregate by glass powder in ...

    glass as fine aggregate will turn this waste material into the valuable resource. Experiments we conducted on concrete prepared by partial replacement of fine aggregate by waste glass powder of particle size 600 micron. The objectives of the investigation evaluate the effect of waste glass

  • GLASS DA 30.07.2016 - SlideShare

    Nov 07, 2016  GLASS DA 30.07.2016 1. DESIGNING CONCRETE MIX OF M25 GRADE BY PARTIAL REPLACEMENT OF FINE AGGREGATE WITH CRUSHED GLASS WASTE Presented By Sanjay T. Chaurasiya Guided by : Prof. Swati Kotulkar Pai Sem-14, Dissertation M.

  • Study the Influence of Waste Glass Powder on the ...

    coarse aggregate is replaced with waste glass powder. From our experimental Investigations we have found that the partial replacement of fine aggregate with waste glass powder yields more compressive strength, when compared to the partial replacement of Coarse aggregate, because the glass powder has more tendency to fill the

    Published in: IOSR Journal of Mechanical and Civil Engineering 2014Authors: K Madhangopal B Nagakiran S R Sraddha G Vinodkumar P Thajun S A Kishor
  • Studies on Glass Powder as Partial Replacement of Cement ...

    partial replacement of cement by waste glass powder of particle size 75µm.The the waste glass powder was replaced by 10%, 20%, 30% and 40% of the binder and the mix design was prepared. The physical and chemical characteristic was studied and the chemical components of the glass powder used in the concrete were also determined by XRF (IIker ...

  • Investigation on Partial Replacement of Coarse Aggregate ...

    strength and flexural strength of concrete by using E-Waste as a partial replacement material for coarse aggregate. Different types of conventional cubes with partial replacement of E-waste on a percentage of 5%, 10%, 15%, 20%, 25% and 30% to coarse aggregate

  • EXPERIMENTAL STUDY ON PARTIAL REPLACEMENT OF FINE

    studies on RC beam by partial replacement of coarse aggregate by crushed waste glass and RCA”, International Journal of Research and Reviews in Applied Sciences and Engineering, Vol.8, No.2, 320-335. [3] Srivastav, A. K. (2016) “Partial replacement of fine aggregates by using waste glass”,

  • Effect of Using Glass Powder in Concrete - rroij

    waste materials as partial replacement of coarse or fine aggregates and cement. Waste glass is one materials when ground to a very fine powder shows pozzolanic properties which can be used as a partial replacement for cement in concrete. In this paper, an attempt has been made to find out the strength of concrete containing waste glass powder ...